Title | Structure and Properties of Superhard (Zr-Ti-Cr-Nb)N Coatings |
Authors |
Postolnyi, Bohdan Oleksandrovych
Bondar, Oleksandr Viacheslavovych Kravchenko, Yuliia Anatoliivna Shypylenko, A.P. Sobol, O.V. Beresnev, V.M. Wegierek, P. Smirnova, K. Kravchenko, Ya. |
ORCID |
http://orcid.org/0000-0003-3174-0709 http://orcid.org/0000-0003-4147-2824 |
Keywords |
Multielement coatings Nitrides Hardness Friction cohesion Vacuum-arc deposition |
Type | Article |
Date of Issue | 2014 |
URI | http://essuir.sumdu.edu.ua/handle/123456789/37311 |
Publisher | Sumy State University |
License | |
Citation | Proc. NAP 3, 01FNC06 (2014) |
Abstract |
This work presents the results of superhard (Zr-Ti-Cr-Nb)N coatings research. Samples were fabricated by vacuum-arc deposition method (Arc-PVD). Structure, composition and properties of these coatings were studied. The study of coatings was performed using SEM, EDS and XRD. Hardness measurements and adhesion tests were provided. The coatings thickness was up to 6.2 mm. Nanocrystallites sizes ranged from 4 to 7.3 nm. Values of hardness and cohesive strength were H=43.7 GPa and LC=62.06 N respectively. The optimal conditions for coating’s deposition were found. |
Appears in Collections: |
Наукові видання (ЕлІТ) |
Views
Canada
1
China
17
France
2
Germany
128486462
Ireland
7538444
Kazakhstan
1
Lithuania
1
Netherlands
4356
Poland
1
Romania
1548197
Russia
1
Sweden
1
Taiwan
1
Ukraine
74856
United Kingdom
740967512
United States
-1070772563
Unknown Country
22307
Uzbekistan
1
Vietnam
26136
Downloads
Canada
1
China
49
France
1
Germany
2
Ireland
1
Kazakhstan
1
Lithuania
1
Ukraine
190758
United Kingdom
1
United States
-1949440861
Unknown Country
34
Vietnam
1
Files
File | Size | Format | Downloads |
---|---|---|---|
Postolnyi_Bondar_Kravchenko_Shypylenko_Sobol_Beresnev_Wegierek Smirnova_Kravchenko.pdf | 611,39 kB | Adobe PDF | -1949250011 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.