Title | Effect of change in Ba concentration on crystallintiy and dielectric constant of the sol-gel deposited barium strontium titante (BST) films on n-type Si wafer |
Authors |
Tripathi, C.C.
Sharma, C. Sood, S.C. Gupta, J. Singh, D. Singh, S. Sharma, R. |
ORCID | |
Keywords |
(Bax, Sr1 – x)TiO XRD диэлектрическая проницаемость dielectric constant діелектрична проникність sol-gel porcess CV-измерения CV-вимірювання CV-measurement |
Type | Article |
Date of Issue | 2011 |
URI | http://essuir.sumdu.edu.ua/handle/123456789/27856 |
Publisher | Видавництво СумДУ |
License | Copyright not evaluated |
Citation | Effect of change in Ba concentration on crystallintiy and dielectric constant of the sol-gel deposited barium strontium titante (BST) films on n-type Si wafer [Текст] / C.C. Tripathi, C. Sharma, S.C. Sood et al. // Journal of Nano- and Electronic Physics. — 2011. — Vol. 3, № 1, Part V : Proceedings of the International Symposium on Semiconductor Materials and Devices (ISSMD-2011), Vadodara, India, 28-30 January 2011. — P. 851-858. |
Abstract |
Thin (Bax, Sr1 – x)TiO3 (BST) films of different chemical compositions (x 0.3 0.5 & 0.7) were prepared by the sol-gel process using barium acetate,strontium acetate and titanium isopropoxide as metal alkoxides. The titanium isopropoxide was dissolved in acetyl acetone (chelating agent) and mixing the resultant solution with barium and strontium acetate dissolved in
acetic acid solution. The alkoxide group in titanium isopropoxide was replaced by acetate ligand and after hydrolysis and condensation process a complex solution was obtained. This solution was deposited on n-type (111) Si wafers by spin coating and after drying at 350 C the samples were annealed at 700 C in oxygen ambient. The precise control of composition of
different species is important for producing good quality films having high crystallinity and dielectric constant. The crystallinity of the film was found to increase with the increase of Ba concentration as found from X-ray diffraction. The calculated value of dielectric constant from CV
measurements revealed that the film of (Ba0.7, Sr0.3) TiO3 had the maximum dielectric constant as 463 and the surface was examined by SEM.
When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/27856 |
Appears in Collections: |
Журнал нано- та електронної фізики (Journal of nano- and electronic physics) |
Views

1

3

6

2

1

1

106396194

1

1

1

169275

1

1

6

4

1

20

1

1

1

2

6987839

3497768

336858135

460924036

26931
Downloads

29

1

106396195

1

1

1

18046882

1

336858133

460924036

1
Files
File | Size | Format | Downloads |
---|---|---|---|
Tripathi.pdf | 1.18 MB | Adobe PDF | 922225281 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.