Title | Effect of Rapid Thermal Annealing of CIGS Thin Film as an Absorber Layer |
Authors |
Ray, J.R.
Desai, M.S. Panchal, C.J. Rehani, Bharati Mehta, P.K. |
ORCID | |
Keywords |
CIGS thin film Rapid thermal annealing XRD SEM EDS TEM |
Type | Article |
Date of Issue | 2013 |
URI | http://essuir.sumdu.edu.ua/handle/123456789/31007 |
Publisher | Сумський державний університет |
License | Copyright not evaluated |
Citation | J.R. Ray, M.S. Desai, C.J. Panchal, et al., J. Nano- Electron. Phys. 5 No 2, 02013 (2013) |
Abstract |
The influence of rapid post-deposition thermal annealing (500 °C for 2 minutes) on the CIGS thin films of different thicknesses (0.4 to 1.0 m) has been investigated. The deposition of CIGS is carried out using the flash evaporation at the substrate temperature of 250 °C. The as-grown and annealed CIGS is characterized by XRD, SEM, EDS, TEM, optical transmission, reflection, and electrical measurements. Lowering the thickness of CIGS absorber shows the remarkable influence on crystal structure, surface morphology, and composition of the overall film. Further improvement was observed by the rapid annealing process. Cu-rich composition was observed for annealed CIGS thin film having a thickness below 0.6 μm, while for 1.0 m thickness the composition is slightly Cu-poor and the compactly packed faceted grains observed. Optical band gap near to 1.05 eV and the electrical resistivity in the order of 104 Ωcm shows its future use as an absorber layer for CIGS solar cell. Furthermore, an attempt of making CIGS / CdS hetero-structure shows ideal behavior of the Schottky hetero-structure with the ideality factor of 1.5.
When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/31007 |
Appears in Collections: |
Журнал нано- та електронної фізики (Journal of nano- and electronic physics) |
Views

1

2

1963703462

647913653

250165

2030047679

1

5900098

1

1

865765374

1

11

1

1

29040

13

1145256824

2

-1233325744

175507309

1966703

2

1145256827

590238504

-1337526871

266254462

1966701
Downloads

-1337526870

1

1

1963703462

1015352550

5900096

1

1

1

1

4

1

54430

35220185

-1233325737

200

1
Files
File | Size | Format | Downloads |
---|---|---|---|
Ray J.R._TEM.pdf | 808.54 kB | Adobe PDF | 449378328 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.