The Annealing Under 1350 °C of Magnetron Sputtered Coatings on Base AlN-TiB2(TiSi2)

Pohrebniak, Oleksandr Dmytrovych; Bondar, Oleksandr Viacheslavovych; Abadias, G.; Sobol, O.V.; Beresnev, V.M.; Pshyk, A.V.; Kolesnikov, D.A.; Wegierek, P.; Plotnikov, S.V.; Erdybaeva, N.K.

Please use this identifier to cite or link to this item: http://essuir.sumdu.edu.ua/handle/123456789/35424

Or use following links to share this resource in social networks: Recommend this item

Title	The Annealing Under 1350 °C of Magnetron Sputtered Coatings on Base AlN-TiB2(TiSi2)
Authors	Pohrebniak, Oleksandr Dmytrovych Bondar, Oleksandr Viacheslavovych Abadias, G. Sobol, O.V. Beresnev, V.M. Pshyk, A.V. Kolesnikov, D.A. Wegierek, P. Plotnikov, S.V. Erdybaeva, N.K.
ORCID	http://orcid.org/0000-0002-9218-6492 http://orcid.org/0000-0003-3174-0709
Keywords	Magnetron Sputtering Structural-Phase Composition Nanostructure Annealing
Type	Conference Papers
Date of Issue	2013
URI	http://essuir.sumdu.edu.ua/handle/123456789/35424
Publisher	Sumy State University
License
Citation	The Annealing Under 1350 °C of Magnetron Sputtered Coatings on Base AlN-TiB2(TiSi2) [Текст] / A.D. Pogrebnjak, G. Abadias, O.V. Bondar et al. // Nanomaterials: Applications & Properties (NAP-2013) : 3-rd International conference, Alushta, the Crimea, Ukraine, September 16-21, 2013 / Edited by: A. Pogrebnjak. - Sumy : Sumy State University, 2013. - V.2, No2. - 02FNC28
Abstract	The magnetron sputtered coatings on base AlN-TiB2(TiSi2) were investigated in this paper. The ele-ment composition, structural-phase composition, morphology and mechanical properties were investigated before and after annealing of coatings under 1350 °C. The concentration of elements in the coating were changed after annealing under 900 °C and further annealing under 1350 °C (especially after annealing under 1350 °C).The hardness of as-deposited coatings was 15 GPa, but after the annealing under 1350 °C the value of hardness was increased up to (2223.5) GPa. The value of the index viscoplastic was 0,07. The amorphous like structure and high damping properties of the AlN-TiB2(TiSi2) coating makes promising the use of these coatings as a contacting layer in multilayer wear resistant coatings, and as diffusion barriers in the form of independent elements. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/35424