Synthesis of Nano-Structured Polyaniline by Direct Emulsion Polymerization

Haghanifar, M.H.; Pishvaei, M.; Pourmahdian, S.; Pakdel, A.S.

Please use this identifier to cite or link to this item: http://essuir.sumdu.edu.ua/handle/123456789/35633

Or use following links to share this resource in social networks: Recommend this item

Title	Synthesis of Nano-Structured Polyaniline by Direct Emulsion Polymerization
Authors	Haghanifar, M.H. Pishvaei, M. Pourmahdian, S. Pakdel, A.S.
ORCID
Keywords	Emulsion Polymerization Polyaniline Conductivity Polymer Yield
Type	Conference Papers
Date of Issue	2013
URI	http://essuir.sumdu.edu.ua/handle/123456789/35633
Publisher	Sumy State University
License	Copyright not evaluated
Citation	Synthesis of Nano-Structured Polyaniline by Direct Emulsion Polymerization [Текст] / M.H. Haghanifar, M. Pishvaei, S. Pourmahdian, A.S. Pakdel // Nanomaterials: Applications & Properties (NAP-2013): 2-nd International conference, Alushta, the Crimea, September 17-22, 2012 / Edited by: A. Pogrebnjak. - Sumy: Sumy State University, 2013. - V.2, No3. - 03NCNN50
Abstract	A direct emulsion process was performed for the synthesis of an emeraldine salt of polyaniline (PANI) us-ing a novel surfactant, namely cetyl dimethyl ammonium phenyl chloride (CDAPhCl). HCl was used as do-pant and potassium persulfate (KPS)was used as an oxidizing agent. Variation of polymer yield was recorded using conventional gravimetric method and resulting polymer salt was analyzed by FTIR. Average particle size and latex morphology was studied using dynamic light scattering (DLS) and scanning electron microsco-py (SEM).Furthermore, the influence of the reaction time followed by polymer yield on the conductivity of re-sulted PANI salt was investigated. SEM images showed a nanostructured polyaniline and conductivity of the polyaninle film found to be 1.65 S cm-1. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/35633