Title Magnetoresistive properties of multilayer film systems based on Fe/Cu and Fe/Cr
Authors Synashenko, Oksana Volodymyrivna
Panchal, Ch.J.
Protsenko, Ivan Yukhymovych  
Панчал, Ч.Ж.
ORCID http://orcid.org/0000-0003-3351-9303
Keywords film system
magnetoresistance
thermal annealing
плівкова система
магнітоопір
термовідпалювання
пленочная система
магнитосопротивление
термоотжиг
Type Article
Date of Issue 2009
URI http://essuir.sumdu.edu.ua/handle/123456789/3593
Publisher Вид-во СумДУ
License
Citation Synashenko, O.V. Magnetoresistive properties of multilayer film systems based on Fe/Cu and Fe/Cr [Текст] / O.V. Synashenlo, Ch.J. Panchal, I.Yu. Protsenko // Журнал нано- та електронної фізики. — 2009. — № 3, Т.1. — C. 16-23.
Abstract Досліджені магніторезистивні властивості багатошарових плівкових систем на основі Fe і Cu або Cr при кімнатній температурі. Вивчені фактори, які впливають на зміну величини магнітоопору (МО). В плівковій системі Fe/Cu, в якій зберігається індивідуальність окремих шарів, перехід від аморфної підкладки із ситалу до монокристалічної Si(111) веде до збільшення величини МО на 35 %, що пов’язано з магнітним упорядкуванням в нижньому епітаксійному шарі Fe. Термічне відпалювання зразків до 700 К призводить до руйнування непарного ефекту в МО в перпендикулярній геометрії та збільшення його величини в 2 рази в паралельних геометрія. Дослідження системи [Fe(dFe)/Cr(1)]10 показали, що збільшення товщини шару Fe від 0,31 до 1,5 нм призводить до збільшення величини МО від 0,03-0,05 % до 1-3 % в залежності від геометрії вимірювання, що пояснюється утворенням гранул Fe в матриці твердого розчину (Fe, Cr). При цитуванні документа, використовуйте посилання http://essuir.sumdu.edu.ua/handle/123456789/3593
The magnetoresistive properties of multilayer film systems based on Fe and Cu or Cr were investigated at room temperature. Factors influencing on magnetoresistance (MR) value changing were studied. In Fe/Cu film system, in which the individuality of separate layers holds, the change of substrate from amorphous pyroceramic to monocrystalline Si(111) leads to MR ratio increasing on 35 %, that is connected with magnetic ordering in bottom epitaxial Fe layer. Thermal annealing of samples to 700 K leads to vanishing of odd effect in MR in perpendicular geometry and MR increasing by two times in parallel geometries. Investigations of [Fe(dFe)/Cr(1)]10 system showed, that the Fe thickness changes from 0,31 to 1,5 nm lead to the magnetoresistance magnitude changes from 0,03-0,05 % to 1-3 % subject to different measurement geometries, which is interpreted by Fe granules formation in matrix of solid solution (Fe, Cr). При цитировании документа, используйте ссылку http://essuir.sumdu.edu.ua/handle/123456789/3593
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

China China
470
Czechia Czechia
1
France France
1
Germany Germany
32486816
Greece Greece
394314
India India
1
Ireland Ireland
6965246
Lithuania Lithuania
1
Moldova Moldova
1
Netherlands Netherlands
65725
Russia Russia
18
Singapore Singapore
-1984645622
Slovakia Slovakia
2
Sweden Sweden
1
Turkey Turkey
8
Ukraine Ukraine
416953009
United Kingdom United Kingdom
104372732
United States United States
325676052
Unknown Country Unknown Country
-1097336822
Vietnam Vietnam
394316

Downloads

China China
55
France France
1
Germany Germany
472
Ireland Ireland
1
Lithuania Lithuania
1
Singapore Singapore
1
Ukraine Ukraine
416953009
United Kingdom United Kingdom
1
United States United States
-1984645623
Unknown Country Unknown Country
-1097336821
Vietnam Vietnam
1

Files

File Size Format Downloads
Synashenko.pdf 301.5 kB Adobe PDF 1629938394

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.