Title | Structure and Composition of Near-Surface Layers in the Ion-Implanted NiTi Alloy |
Other Titles |
Структура і склад приповерхневих шарів в іонно-імплантованих NiTi сплавах |
Authors |
Pohrebniak, Oleksandr Dmytrovych
Bratushka, Serhii Mykolaiovych Levintant, N. |
ORCID |
http://orcid.org/0000-0002-9218-6492 http://orcid.org/0000-0003-3470-2265 |
Keywords |
TiNi alloy properties implantation імплантація властивості TiNi сплави |
Type | Article |
Date of Issue | 2010 |
URI | http://essuir.sumdu.edu.ua/handle/123456789/50883 |
Publisher | Publishing House of the IOA SB RAS |
License | |
Citation | Pogrebnjak, A.D. Structure and Composition of Near-Surface Layers in the Ion-Implanted NiTi Alloy [Text] / A.D. Pogrebnjak, S.N. Bratushka, N. Levintant // 10th International Conference on Modification of Materials with Particle Beams and Plasma Flows: proceedings. - Tomsk, 2010. - P. 213-219. |
Abstract |
Поверхностный слой сплава TiNi, обладающего эффектом памяти формы в мартенситном состоянии, изменен высокой дозой имплантированныъ ионов N + ионов (дозы имплантации варьируется от 1017 до 1018 ion/cm2). TiNi образцов, имплантированных N +, Ni +-N +, и Мо +-W + при дозе 10l7-1018 см-2 и изучены обратным рассеяния Резерфорда. сканирующей электронной микроскопией, энергетической дисперсионной спектроскопией, рентгеновской дифракции (скользящей геометрией), и путем измерения нанотвердости и модуль упругости. Ni + концентрации обнаружен пик между двумя максимумами в глубину профиля концентрации ионов N +.
Рентгеновской дифракции образцов TiNi имплантированных Ni + и N + ионов показывает формирование TiNi (B2), олово и Ni3N фаз. В исходном состоянии, модуль упругости образцов E = 56 ГПа при твердости Н = 2,13 ± 03 ГПа (на глубине 150 нм). После двойной имплантации Ni +-N + и Мо +-W + ионов, твердость образцов TiNi является 2,78 ± 0,95 ГПа на глубине 150 нм и 495 ± 2,25 ГПа на глубине 50 нм, модуль упругости 59 ГПа. Отжиг образцов при температуре 550 ° С приводит к увеличению твердости 4,44 ± 1,45 ГПа и резкое увеличение модуля упругости до 236 ± 39 ГПа. Корреляции между элементным составом, микроструктурой и механическими свойствами поверхностного слоя в TiNi не найдено. The surface layer of an equiatomic TiNi alloy, which exhibits the shape memory effect in the martensitic state, is modified with high-dose implantation of 65-keV N+ ions (the implantation dose is varied from 1017 to 1018 ions/cm2). TiNi samples are implanted by N+, Ni+–N+, and Mo+–W+ ions at a dose of 10l7–1018 cm–2 and studied by Rutherford backscattering. scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction (glancing geometry), and by measuring the nanohardness and the elastic modulus. A Ni+ concentration peak is detected between two maxima in the depth profile of the N+ ion concentration. X-ray diffraction (glancing geometry) of TiNi samples implanted by Ni+ and N+ ions shows the formation of the TiNi (B2), TiN and Ni3N phases. In the initial state, the elastic modulus of the samples is E = 56 GPa at a hardness of H = 2.13 ± 03 GPa (at a depth of 150 nm). After double implantation by Ni+–N+ and Mo+–W+ ions, the hardness of the TiNi samples is 2.78 ± 0.95 GPa at a depth of 150 nm and 495 ± 2.25 GPa at a depth of 50 nm; the elastic modulus is 59 GPa. Annealing of the samples at 550 °C leads to an increase in the hardness to 4.44 ± 1.45 GPa and a sharp increase in the elastic modulus to 236 ± 39 GPa. A correlation between the elemental composition, microstructure, shape memory effect, and mechanical properties of the near-surface layer in TiNi is found. |
Appears in Collections: |
Наукові видання (ННІ БТ) |
Views
Australia
1
Canada
1
China
1
France
1
Germany
85317
Greece
1
Ireland
167119
Italy
1
Japan
1
Lithuania
1
Poland
1
Singapore
1
Sweden
1
Ukraine
1727242
United Kingdom
864793
United States
18926154
Unknown Country
1727241
Vietnam
9938
Downloads
Australia
1
China
1
Cuba
1
Germany
3
Ireland
1
Lithuania
1
Ukraine
5181172
United Kingdom
1
United States
18926153
Unknown Country
1
Vietnam
1
Files
File | Size | Format | Downloads |
---|---|---|---|
Pogrebnjak_Structure_and_Composition.pdf | 3.51 MB | Adobe PDF | 24107336 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.