Title Thickness Dependent Magnetic Study of Fe Thin Films
Other Titles Дослідження залежних від товщини магнітних властивостей тонких плівок Fe
Authors Brajpuriya, R.
Vij, A.
Sharma, Ram K.
ORCID
Keywords тонка плівка Fe
VSM
магнітні властивості
електронно-променеве випаровування
Fe thin film
magnetic properties
electron beam evaporation
Type Article
Date of Issue 2021
URI https://essuir.sumdu.edu.ua/handle/123456789/85290
Publisher Sumy State University
License In Copyright
Citation R. Brajpuriya, A. Vij, Ram K. Sharma, J. Nano- Electron. Phys. 13 No 4, 04005 (2021). DOI: https://doi.org/10.21272/jnep.13(4).04005
Abstract У роботі вивчено магнітні властивості плівок Fe різної товщини (150, 200, 300 і 400 Å), нанесених на підкладку з термополірованого скла методом електронно-променевого (EB) осадження. Дослідження було спричинене відсутністю даних про нанесені випаровуванням плівки Fe у заданому діапазоні товщин. Для порівняння також було досліджено магнітні властивості плівки Fe товщиною 300 Å, нанесеної методом іонно-променевого напилення (IBS). Магнітні властивості, такі як коерцитивність, намагніченість насичення, залишкова намагніченість тощо, були отримані з аналізу петель M-H при кімнатній температурі, а варіація цих параметрів корелювала з товщиною плівки. Всі плівки демонструють високу анізотропію по відношенню до вирівнювання спінів, причому майже всі спіни лежать у площині плівки. Систематичне збільшення намагніченості насичення спостерігається із збільшенням товщини зразка. Магнітні властивості плівки IBS не сильно відрізняються від властивостей зразків EB, за винятком зменшення коерцитивності на 11 %, яке можна пояснити меншою шорсткістю плівки IBS. Це відображається у коефіцієнті прямокутності, що приблизно дорівнює 1 для всіх зразків.
In the present work, studies of the magnetic properties of Fe films of various thickness (150, 200, 300, and 400 Å) deposited on float glass substrate by electron beam (EB) deposition technique are reported. The investigation was prompted by the lack of data on evaporated Fe films in this thickness regime. For comparison, the magnetic properties of a Fe film deposited by ion beam sputtering (IBS) technique of a thickness of 300 Å have also been investigated. Magnetic properties like coercivity, saturation magnetization, retentivity etc. have been obtained by analysis of M-H loops recorded at room temperature, and the variation in these parameters has been correlated to the film thickness. All the films show high anisotropy with respect to spin alignment with nearly all the spins lying in the plane of the film. A systematic increase in the saturation magnetization is observed with an increase in sample thickness. The magnetic properties of the IBS film are not very different from the EB samples except for a 11 % decrease in the coercivity which can be attributed to lesser roughness of the IBS film. This is reflected in the squareness ratio of nearly 1 for all the samples.
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

China China
1027058713
France France
1
Germany Germany
1
Ghana Ghana
1
India India
11768737
Ireland Ireland
6214291
Lithuania Lithuania
1
Mexico Mexico
329923
Pakistan Pakistan
1
South Korea South Korea
1
Taiwan Taiwan
1
Ukraine Ukraine
95202370
United Kingdom United Kingdom
38434258
United States United States
2054113269
Unknown Country Unknown Country
95202369

Downloads

Belgium Belgium
1
China China
779902598
France France
532746486
Germany Germany
38434256
India India
38434258
Ireland Ireland
3437067
Lithuania Lithuania
1
Mexico Mexico
532746487
Singapore Singapore
4158
South Korea South Korea
1
Switzerland Switzerland
1
Thailand Thailand
1
Ukraine Ukraine
285590372
United Kingdom United Kingdom
1
United States United States
-966643357
Unknown Country Unknown Country
1

Files

File Size Format Downloads
Brajpuriya_jnep_4_2021.pdf 390.62 kB Adobe PDF 1244652332

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.