Title Hydrochemical Synthesis of HgS1 – xSex Film Solid Solutions
Other Titles Гідрохімічний синтез плівкових твердих розчинів HgS1 – xSex
Authors Sozanskyi, M.A.
Shapoval, P.Yo.
Stadnik, V.E.
Kyrulo, O.P.
Laruk, M.M.
ORCID
Keywords сульфід ртуті
селенід ртуті
плівки
тверді розчини
хімічне осадження
оптичні властивості
mercury sulfide
mercury selenide
films
solid solution
chemical deposition
optical properties
Type Article
Date of Issue 2021
URI https://essuir.sumdu.edu.ua/handle/123456789/85993
Publisher Sumy State University
License In Copyright
Citation M.A. Sozanskyi, P.Yo. Shapoval, V.E. Stadnik, et al., J. Nano- Electron. Phys. 13 No 5, 05032 (2021). DOI: https://doi.org/10.21272/jnep.13(5).05032
Abstract Плівки твердого розчину сульфіду-селеніду ртуті (HgS1 – xSex) синтезовано на скляних підкладках методом гідрохімічного осадження. Використано водні розчини нітрату ртуті (II), тіосечовини, натрій селеносульфату та тринатрій цитрату. Проведено теоретичний розрахунок граничних умов утворення сульфіду ртуті, селеніду ртуті та оксиду ртуті в системі ртуть-тіосечовина-цитрат. Згідно з виконаним рентгенофазовим та елементним аналізом, отримані зразки плівок є однофазними і складаються із твердих розчинів заміщення HgS1 – xSex. Досліджено вплив концентрації селеносульфату натрію на ступінь заміщення S-Se покриттів HgS1 – xSex. Встановлено, що параметр x змінюється від 0.068 до 0.334 із збільшенням вмісту Na2SeSO3 від 1·10 – 5 до 1·10 – 4 М. В той же час, модифікація структури HgS1 – xSex змінюється з кіновару до сфалериту. Більш високі концентрації селеносульфату натрію дають занадто високу швидкість формування кінцевого продукту, і, відповідно, складність отримання покриттів. Досліджено морфологічні та оптичні властивості плівок HgS1 – xSex. Їхня поверхня є суцільною, однорідною і має невелику кількість поверхневих дефектів. Оптичне пропускання плівок HgS1 – xSex збільшується в досліджуваній області довжин хвиль від 340 до 900 нм. Крива пропускання має стрибок в області 400 нм, який зміщується вправо зі збільшенням вмісту селену в HgS1 – xSex, відповідно, оптична ширина забороненої зони плівок зменшується з 2.70 до 2.43 еВ.
Solid solution films of mercury sulfide-selenide (HgS1 – xSex) were synthesized on glass substrates by the hydrochemical deposition method. Aqueous solutions of mercury (II) nitrate, thiourea, sodium selenosulfate and trisodium citrate were used. Theoretical calculations of the boundary conditions for the formation of mercury sulfide, mercury selenide and mercury oxide were made in the mercury-thiourea-citrate system. According to the performed X-ray and elemental analysis, the obtained film samples are single phase and consist of HgS1 – xSex substitutional solid solutions. The effect of sodium selenosulfate concentration on the S-Se degree of substitution of HgS1 – xSex coatings was investigated. It was established that the x parameter changes from 0.068 to 0.334 with increasing Na2SeSO3 content from 1·10 – 5 to 1·10 – 4 M. At the same time, the HgS1 – xSex structure modification changes from cinnabar to sphalerite. Higher concentrations of sodium selenosulfate give too high formation rate of the final product and, accordingly, it is difficult to obtain coatings. The morphological and optical properties of HgS1 – xSex films were examined. Their surface is solid, smooth and has a small amount of surface defects. The optical transmission of HgS1 – xSex films increases in the investigated wavelength range from 340 to 900 nm. The transmission curve has a jump in the 400 nm region, which shifts to the longer wavelength region with increasing selenium content in HgS1 – xSex, accordingly, the optical band gap of the films decreases from 2.7 to 2.43 eV.
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

China China
1
Czechia Czechia
1
Egypt Egypt
8391901
France France
1
Germany Germany
1
Greece Greece
265
Iran Iran
1
Ireland Ireland
3301
Italy Italy
1
Japan Japan
58555305
Lithuania Lithuania
1
Mongolia Mongolia
1
Singapore Singapore
1
Somalia Somalia
1
Sweden Sweden
1
Ukraine Ukraine
8391900
United Kingdom United Kingdom
191846
United States United States
210887786
Unknown Country Unknown Country
287054028
Vietnam Vietnam
268
Yemen Yemen
1

Downloads

Algeria Algeria
9816
China China
23333434
France France
210887785
Germany Germany
191841
Ireland Ireland
9815
Lithuania Lithuania
1
Singapore Singapore
210887790
South Korea South Korea
1
Ukraine Ukraine
40944368
United Kingdom United Kingdom
1
United States United States
210887788
Unknown Country Unknown Country
210887786
Vietnam Vietnam
1

Files

File Size Format Downloads
Sozanskyi_jnep_5_2021.pdf 1.52 MB Adobe PDF 908040427

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.