Title Crystal Structure of ZnxCd1-xS Nanocrystals Obtained by Self-Propagating High-Temperature Synthesis
Other Titles Кристалічна структура нанокристалів ZnxCd1-xS, отриманих шляхом саморозповсюджуваного високотемпературного синтезу
Authors Kovalenko, А.V.
Plakhtii, Ye.G.
Khmelenko, О.V.
ORCID
Keywords нанокристали ZnxCd1-xS
сульфід цинку
сульфід кадмію
саморозповсюджуваний високотемпературний синтез
рентгеноструктурний аналіз
спектри ЕПР
кристалічна структура
ZnxCd1-xS nanocrystals
zinc sulfide
cadmium sulfide
self-propagating high-temperature synthesis
X-ray diffraction analysis
EPR spectra
crystal structure
Type Article
Date of Issue 2022
URI https://essuir.sumdu.edu.ua/handle/123456789/87453
Publisher Sumy State University
License In Copyright
Citation А.V. Kovalenko, Ye.G. Plakhtii, О.V. Khmelenko, J. Nano- Electron. Phys. 14 No 1, 01017 (2022). DOI: https://doi.org/10.21272/jnep.14(1).01017
Abstract Нанокристали ZnxCd1-xS були отримані методом саморозповсюджуваного високотемпературного синтезу. Синтез проводили в повітряному середовищі за атмосферного тиску. Нам вдалося синтезувати нанокристали, близькі до CdS (0 ≤ x < 0,2), а також близькі до ZnS (0,8 ≤ x ≤ 1), змінюючи співвідношення Zn і Cd з 0 до 1 з кроком 0,1 у реальному продукті. Їх розміри визначали за методом Шеррера і знаходилися в межах 40÷60 ± 5 нм. Нанокристали ZnxCd1-xS усіх складів характеризувались змішаною кристалічною структурою; максимальна частка кубічної фази характерна для складів, близьких до ZnS, а мінімальна – для складів, близьких до CdS. Ступені мікродеформації кристалічної решітки нанокристалів ZnxCd1-xS були в межах 1,05·104÷3,97·103; густину дислокацій визначали в межах 7,91·1010÷3,1·1011. На основі аналізу спектрів ЕПР було показано, що при зміні локального оточення іонів Mn2+ із збільшенням параметра x константа надтонкої структури ЕПР іонів Mn2+ стрибкоподібно зменшувалася від значення А = 7,00÷7,06 мТ до значення А = 6,84 мТ. Наявність лінії ЕПР іонів Cr+ у неосвітлених нанокристалах ZnS та Zn0,8Cd0,2S може побічно вказувати на провідність n-типу отриманих зразків.
ZnxCd1-xS nanocrystals were obtained by self-propagating high-temperature synthesis. The synthesis was carried out in an air environment at atmospheric pressure. We managed to synthesize nanocrystals close to CdS (0 ≤ x < 0.2), as well as close to ZnS (0.8 ≤ x ≤ 1) by changing the ratio between Zn and Cd from 0 to 1 with a step of 0.1 in a real product. Their sizes were determined by the Scherrer method and were in the range of 40÷60 ± 5 nm. ZnxCd1-xS nanocrystals of all compositions were characterized by a mixed crystal structure; the maximum proportion of the cubic phase was typical of compositions close to ZnS, and the minimum one – of compositions close to CdS. The degrees of microdeformations of the crystal lattice of ZnxCd1-xS nanocrystals were within 1.05∙104÷3.97∙103; dislocation densities were determined within 7.91∙1010÷3.1∙1011. Based on the analysis of the EPR spectra, it was shown that when the local environment of Mn2+ ions changed with increasing parameter x, the constant of the EPR hyperfine structure of Mn2+ ions explosively decreased from the value А = 7.00÷7.06 mТ to the value А = 6.84 mТ. The presence of the EPR line of Cr+ ions in unlit ZnS and Zn0.8Cd0.2S nanocrystals may indirectly indicate n-type conductivity of the samples obtained.
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

Australia Australia
1
China China
72994399
Denmark Denmark
882
Finland Finland
389
Greece Greece
1
Ireland Ireland
1577556
Lithuania Lithuania
1
Singapore Singapore
1
Ukraine Ukraine
584694788
United Kingdom United Kingdom
24331467
United States United States
739715223
Unknown Country Unknown Country
206397623
Vietnam Vietnam
439

Downloads

Canada Canada
1
China China
-1040279870
Denmark Denmark
883
France France
-1040279869
Germany Germany
24331465
India India
1
Ireland Ireland
1
Japan Japan
1
Lithuania Lithuania
1
Switzerland Switzerland
1
Ukraine Ukraine
584694789
United Kingdom United Kingdom
1
United States United States
1629712772
Unknown Country Unknown Country
739715226
Vietnam Vietnam
1

Files

File Size Format Downloads
Kovalenko_jnep_1_2022.pdf 518.81 kB Adobe PDF 897895404

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.