Title Физико-химические и триботехнические свойства железа, оплавленного импульсной плазменной струей
Other Titles Physical and chemical properties of Fe by pulse plasma jet melted
Authors Bratushka, Serhii Mykolaiovych  
Pohrebniak, Oleksandr Dmytrovych  
Тюрин, Ю.Н.
ORCID http://orcid.org/0000-0003-3470-2265
http://orcid.org/0000-0002-9218-6492
Keywords микротвердость
легирование
плазменная струя
microhardness
plasma jet melted
Type Article
Date of Issue 2007
URI http://essuir.sumdu.edu.ua/handle/123456789/55256
Publisher
License
Citation Физико-химические и триботехнические свойства железа, оплавленного импульсной плазменной струей [Текст] / А.Д. Погребняк, С.Н. Братушка, А.Д. Михалев, Н.К. Ердыбаева, О.В. Колисниченко, Ю.Н. Тюрин // Трение и износ. - 2007. – № 5. - Т. 28. – С. 457–464.
Abstract Представлені результати досліджень физико-хімічних і тріботехнічних властивостей зразків Fe, оплавлених і легованих за допомогою плазмового струменя. Мікротвердість оплавлених зразків зросла в 2,5 разу в порівнянні з початковими, а їх зношування при терті стало в 2 рази нижче від початкового. Приповерхневий шар заліза легований елементами, що містяться в електроді: W, Co, Cu. Разом з а-Fe в поверхневому шарі утворюються мілкодисперсні карбіди Fe6W6C, а також, можливо, W6Co6C. Після випробувань на зношування на глибині 15 мкм від поверхні тертя легованого Fe виявлено до 1,2 ат.W. Result of studies, which were performed using iron samples (0.08 zhf) treated by a pulsed plasma jet. A hard alloy WC–Co, which additionally doped the sample surface at the moment of melting of a surface iron layer, was used as an eroding electrode. In the surface layer we found Fe6W6C carbides of small dimension ranges and Fe, Co and Co6W6C. W concentration in the surface (micro- and nanocrystal) layer reached 8.5 at. Co concentration changed from 16 to 32 at. We also found that friction wear resistance increased be a factor of three, nano- and microhardness was minimum 2.0 GPa to 7.9 GPa.
Appears in Collections: Наукові видання (ННІ БТ)

Views

China China
1
France France
3
Germany Germany
5450857
Ireland Ireland
395731
Lithuania Lithuania
1
Netherlands Netherlands
4472
Singapore Singapore
1
Sweden Sweden
1
Ukraine Ukraine
67317193
United Kingdom United Kingdom
30732353
United States United States
-1755965477
Unknown Country Unknown Country
336583125

Downloads

China China
2
Germany Germany
52
Indonesia Indonesia
1
Ireland Ireland
1
Kazakhstan Kazakhstan
1
Lithuania Lithuania
1
Sweden Sweden
1
Ukraine Ukraine
777066864
United Kingdom United Kingdom
1
United States United States
-1755965478
Unknown Country Unknown Country
4

Files

File Size Format Downloads
Fyzyko-khymycheskye.pdf 972.2 kB Adobe PDF -978898550

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.