Title Tribotechnical Properties of (TiZr)N/(TiSi)N Multilayer Coatings with Nanometer Thickness
Other Titles Триботехнічні властивості багатошарових покриттів (TiZr)N/(TiSi) N з нанометровою товщиною
Authors Beresnev, V.M.
Lytovchenko, S.V.
Horokh, D.V.
Mazilin, B.O.
Stolbovoy, V.A.
Kolodiy, I.N.
Kolesnikov, D.A.
Grudnitsky, V.V.
Srebniuk, P.A.
Glukhov, О.V.
ORCID
Keywords вакуумне дугове осадження
багатошарові нітридні покриття
структура
коефіцієнт тертя
твердість
vacuum arc deposition
multilayer nitride coatings
structure
friction coefficient
hardness
Type Article
Date of Issue 2019
URI http://essuir.sumdu.edu.ua/handle/123456789/75232
Publisher Sumy State University
License
Citation Tribotechnical Properties of (TiZr)N/(TiSi)N Multilayer Coatings with Nanometer Thickness [Текст] = Триботехнічні властивості багатошарових покриттів (TiZr)N/(TiSi) N з нанометровою товщиною / V.M. Beresnev, S.V. Lytovchenko, D.V. Horokh [et al.] // Журнал нано- та електронної фізики. - 2019. - Т. 11, № 5. - 05037. - DOI: 10.21272/jnep.11(5).05037.
Abstract Досліджено триботехнічні характеристики багатошарових нітридних покриттів (TiZr)N/(TiSi)N, отриманих методом вакуум-дугового осадження при кімнатній температурі. Проведено аналіз впливу умов осадження покриттів на механічні та трибологічні властивості покриттів з різними періодами модуляції (загальна товщина двошарового шару) цієї структури: у 1-й серії з λ близько 20.4 нм, у 2-й серії з λ ≈ 43,9 нм, і в 3-й серії зразків формувалося покриття товщиною λ ≈ 137 нм. Результати зносу були досліджені, і вони свідчать про те, що багатоелементні нітридні покриття зношуються за абразивним механізмом. Інтенсивність зносу в покриттях з кількістю шарів 360 (період λ = 20,4 нм) у 2 рази нижча, ніж в покриттях з 89 шарами (період λ = 137 нм). Значення коефіцієнта тертя під час випробувань становили 0,79-0,82. Твердість покриттів становила HV0.05 = 37.6 ГПа для зразків першої серії, HV0.05 = 31.2 ГПа для зразків другої серії та HV0.05 = 26.5 ГПа для зразків третьої серії.
The tribotechnical characteristics of (TiZr)N/(TiSi)N nitride multilayer coatings obtained by the method of vacuum-arc deposition at room temperature were investigated. The analysis of the influence of the deposition conditions on the mechanical and tribological properties of coatings with different modulation periods (total bilayer thickness) of this structure was carried out: in the 1st series λ about 20.4 nm, in the 2nd series with λ ≈ 43.9 nm, and in the 3d series of samples the coating was formed with a thickness of λ ≈ 137 nm. The results of wear were investigated, and they indicate that multi-element nitride coatings wear out by abrasive mechanism. The intensity of wear in coatings with the number of layers 360 (period λ = 20.4 nm) is 2 times lower than in coatings of 89 layers (period λ = 137 nm). The values of the friction coefficient were 0.79-0.82 during tests. Coating hardness was HV0.05 = 37.6 GPa for the samples of series 1, HV0.05 = 31.2 GPa for the second series, and HV0.05 = 26.5 GPa for the samples of series 3.
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

Canada Canada
1
China China
1
Greece Greece
1
Ireland Ireland
3411
Lithuania Lithuania
1
Netherlands Netherlands
200
Ukraine Ukraine
48246
United Kingdom United Kingdom
24473
United States United States
269217
Unknown Country Unknown Country
48245

Downloads

Ireland Ireland
1
Lithuania Lithuania
1
Ukraine Ukraine
144637
United Kingdom United Kingdom
1
United States United States
48244

Files

File Size Format Downloads
Beresnev_jnep_5_2019.pdf 442,13 kB Adobe PDF 192884

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.