Видання зареєстровані авторами шляхом самоархівування
Permanent URI for this communityhttps://devessuir.sumdu.edu.ua/handle/123456789/1
Browse
2 results
Search Results
Item Electric-Spark Alloying of Metal Surfaces with Graphite(G. V. Kurdyumov Institute for Metal Physics of the N.A.S. of Ukraine, 2022) Tarelnyk, V. B.; Гапонова, Оксана Петрівна; Гапонова, Оксана Петровна; Haponova, Oksana Petrivna; Konoplianchenko, Ye.V.The article reviews and analyses the current scientific research in the field of surface treatment of metal surfaces with concentrated energy fluxes (CEF) — the electric-spark (in the literature, known also as electrospark) alloying (ESA), which makes it possible to obtain surface structures with unique physical, mechanical and tribological properties at the nanoscale. The ESA method with a graphite electrode (electrospark carburizing — EC) is based on the process of diffusion (saturation of the surface layer of a part with carbon), and it is not accompanied by an increase in the size of the part. In this article, the influence of the EC parameters on the quality of the carburized layer is investigated. The microstructural analysis shows that the three characteristic zones could be distinguished in the structure: the carburized (‘white’) layer, the finely dispersed transition zone with fine grain, and the base metal zone. The analysis of the results of the durometric studies of the coatings is carried out. To achieve the required parameters of dimensional accuracy and roughness of the working surface of the part after the EC process, it is necessary to use the method of non-abrasive ultrasonic finishing (NAUF). In addition, because of applying the NAUF method, the surface roughness is decreased, the tensile stresses are changed to the compressive ones, and the fatigue strength is increased too. In addition, to reduce the roughness of the treated surface, it is proposed to apply the EC technology in stages, reducing the energy of the spark discharge at each subsequent stage. In order to increase the quality of the carburized layer obtained by the EC process, it is proposed to use a graphite powder, which is applied to the treated surface before alloying. The comparative analysis shows that, after the traditional EC process at Wp = 4.6 J, the surface roughness of steel 20 is Ra = 8.3–9.0 μm, and after the proposed technology, Ra = 3.2–4.8 μm. In this case, the continuity of the alloyed layer increases up to 100%; there increases the depth of the diffusion zone of carbon up to 80 μm as well as the microhardness of the ‘white’ layer and its thickness, which increase up to 9932 MPa and up to 230 μm, respectively. The local micro-x-ray spectral analysis of the obtained coatings shows that, at the EC process carried out in a traditional way, the applying Wp = 0.9, 2.6, 4.6 J provides the formation of the surface layers with high-carbon content depths of 70, 100, 120 μm, respectively, and with the use of a graphite powder, they are of 80, 120, 170 μm. While deepening, the amount of carbon is decreasing from 0.72–0.86% to the carbon content in the base metal — 0.17–0.24%. In the near-surface layer formed with the use of the new technology, the pores are filled with free graphite, which could be used as a solid lubricant to improve the operating characteristics of the friction-pairs parts processed thereby.Item Цементація сталевих деталей електроіскровим леґуванням(Інститут металофізики ім. Г. В. Курдюмова НАН України, 2020) Тарельник, В`ячеслав Борисович; Тарельник, Вячеслав Борисович; Tarelnyk, Viacheslav Borysovych; Гапонова, Оксана Петрівна; Гапонова, Оксана Петровна; Haponova, Oksana Petrivna; Кирик, Г.В.; Коноплянченко, Є.В.; Тарельник, Н.В.; Мікуліна, М.О.Розглянуто спосіб цементації методом електроіскрового леґування (ЦЕІЛ). Досліджувалися зразки зі сталі 20. Як методи дослідження використовували металографічний, дюрометричний, мікрорентґеноспектральний аналізи та дослідження шорсткості поверхні. Показано, що традиційна технологія ЦЕІЛ графітовим електродом не дозволяє отримати покриття високої якості. Запропонована нова технологія ЦЕІЛ, що полягає в поетапному обробленні зразків: на першому етапі здійснюється ЦЕІЛ поверхні зразка відповідно до обраної енергії розряду і з продуктивністю 1 см2/хв; на другому етапі на сформовану на першому етапі поверхню деталі наносять, ретельно втираючи, порошок графіту у вигляді суспензії, виготовленої у співвідношенні ≅80% порошку графіту і 20% вазеліну; на третьому етапі, не чекаючи висихання, проводять ЦЕІЛ сформованої на другому етапі поверхні, причому на тому ж режимі і з такою ж продуктивністю, як і на першому етапі. Порівняльний аналіз якісних параметрів шару після традиційної і пропонованої технологій ЦЕІЛ показав, що після обробки поверхні за пропонованою технологією шорсткість поверхні зменшується з 8,3–9,0 мкм до 3,2–4,8 мкм, збільшується суцільність леґованого шару до 100% та глибина дифузійної зони Вуглецю до 80 мкм, а також мікротвердість «білого» шару і його товщина до 9932 МПа і до 230 мкм відповідно.