Changing of defect’s structure and properties of superhard nanostructured Ti-Si-N coatings, fabricated using CPVD, before and after annealing

No Thumbnail Available

Date

2013

Journal Title

Journal ISSN

Volume Title

Publisher

Scientific Research
Article

Date of Defense

Scientific Director

Speciality

Date of Presentation

Abstract

Using such unique methods of analysis as slow positron beam (SPB), RBS, μ-PIXE (proton microbeam), XRD, SEM with EDS, XPS, nanohardness and elastic modulus measurements, we studied superhard nanostructure Ti-Si-N coatings, which were deposited using Cathodic-PVD method, before and after annealing at the temperature of 600°C for 30 minutes. It is shown in the paper that redistribution of N and Si occurs on the borders of nanograins after annealing, amorphous phase α-SiNx (Si3N4) is created, defects segregates on interfaces and forms vacancy-type clusters with rather high concentration from 5 × 10[16] cm-3 to 7.5 × 10[17] cm-3 due to thermodiffusion. Solid solution (Ti,Si)N and small concentration of α-SiN (close to XRD detection limits) are formed in the coating. Also it was obtained, that deflected mode is formed in the coating (compressive deformation equals to –2.6%), but after thermal annealing deformation reduces to a value of -2.3%. Size of nanograins of solid solution (Ti, Si)N increases from 12.5 nm to (13.2 ÷ 13.4) nm. 25 nm size grains increase their size to 28.5 nm after annealing (under another deposition regime). When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/33948

Keywords

Nanostructure, Wear, Nanohardness, Profiles of Defects, Ti-Si-N

Citation

Changing of defect’s structure and properties of superhard nanostructured Ti-Si-N coatings, fabricated using CPVD, before and after annealing [Текст] / O.D. Pohrebniak, O.V. Bondar, O.V. Sobol, V.M. Beresnev // Soft Nanoscience Letters. — 2013. — №3. — P. 46-51

Endorsement

Review

Supplemented By

Referenced By