Title: Properties of Multilayered Nanoscale TiN/MoN Coatings, Fabricated Using Arc Evaporation
Authors: Pohrebniak, Oleksandr Dmytrovych 
Bondar, Oleksandr Viacheslavovych 
Abadias, G.
Eyidi, D.
Zhollybekov, B.
Keywords: TiN
MoN
multilayer
nanocomposite
nanograin
hardness
Issue Year: 2014
Publisher: Sumy State University
Citation: Proc. NAP 3, 01NTF23 (2014)
Abstract: Using vacuum-arc evaporation method we fabricated periodic multilayered TiN/MoN coatings with different bilayer periods ranging from 8 to 100 nm. We found that MoN and TiN layers grown on steel substrate show local partial epitaxy and columnar growth across interfaces. A Mo-Ti-C interlayer was observed between the substrate and the multilayered coating. MoN and TiN layers contain small (5÷30 nm) grains and are well crystallized with (100) preferred orientation. They were identified as stoichiometric fcc TiN and cubic γ-Mo2N. Non-cubic molybdenum nitride phases were also detected. The hardness of the obtained structures achieved great values and maximal hardness was 31÷41.8 GPa for multilayered structure with 8 nm period. Fabricated coatings are perspective for using as protective coatings in order to improve mechanical characteristics of different construction materials.
URI: http://essuir.sumdu.edu.ua/handle/123456789/37169
Type: Article
Appears in Collections:Наукові видання (ЕлІТ)

Views
Other111
Canada1
China18
Czech Republic3
Germany4
Finland1
France3
Italy1
Netherlands1
Ukraine3
United States2
Uzbekistan2
Downloads
Other24
China67
Czech Republic2
Germany2
Finland1
France1
Italy1
Poland2
Uzbekistan2


Files in This Item:
File Description SizeFormatDownloads 
Pogrebnjak_ Bondar_Abadias_ Eyidi_Zhollybekov.pdf552.84 kBAdobe PDF102Download


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.