Title Formation Processes of Nanocomposite Strengthening Particles in Rapidly Quenched Al-Sc-Zr Alloys
Authors Berezina, A.L.
Monastyrska, T.O.
Molebny, O.A.
Nosenko, V.K.
Kotko, A.V.
ORCID
Keywords The rapid quenching from the liquid State
Anomalous supersaturated solid solution
Type Article
Date of Issue 2012
URI http://essuir.sumdu.edu.ua/handle/123456789/24888
Publisher Видавництво СумДУ
License
Citation A.L. Berezina, T.O. Monastyrska, O.A. Molebny et al. J. Nano-Electron. Phys. 4 No 1, 01006 (2012)
Abstract Decomposition processes of supersaturated solid solution of aluminium alloys alloyed with Sc and Zr have been studied in the work. The binary hypereutectic Al-Sc alloys, hyperperitectic Al-Zr alloys and ternary Al-Sc-Zr alloys were chosen. Alloys were obtained by the melt-spinning. Melts were quenched from temperatures of Т = 1000 C and Т = 1400 ºC. The study of the structure of rapidly solidifyed binary Al alloys alloyed with Sc and Zr showed that the crystallization of anomalously supersaturated solid solution (Tquen. = 1400 ºC) or the crystallization with the formation of "fan" structure (Tquen. = 1000 ºC) are possible depending on the quenching temperature of the melt. The decomposition of anomalously supersaturated solid solution is continuous, with the precipitation of nano-sized spherical Al3X (X-Sc, Zr) particles of L12-ordered phase which is isomorphous to matrix. It was found that the loss of thermal stability of Al-Sc alloys is due to the loss of coherence of the strengthening Al3Sc phase. In Al-Zr alloys the loss of strength is due to the formation of a stable tetragonal DO23-ordered A13Zr phase. After co-alloying of Al by Sc and Zr a bimodal grained structure was observed for the hypereutectic ternary alloy (Tquen. = 400ºC). Nano-sized grains of 50-60 nm were present on the boundaries of 1-2 µm large-sized grains. TEM shows the formation of nanocomposite Al3Zr/Al3Sc particles. The formation of Al3Zr shell changes the nature of the interfacial fit of the particle with the matrix and slows down the decomposition during the coalescence. Ternary Al-Sc-Zr alloys have significantly higher thermal stability during aging as compared to binary Al-Sc and Al-Zr alloys. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/24888
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

Australia Australia
1
Canada Canada
30352723
China China
15176372
Cyprus Cyprus
1
Estonia Estonia
1
Germany Germany
-2134958944
Greece Greece
164048
India India
2
Iran Iran
2
Ireland Ireland
1341814
Lithuania Lithuania
1
Moldova Moldova
1
Netherlands Netherlands
16828
Portugal Portugal
1
Russia Russia
23
Singapore Singapore
1081345990
South Korea South Korea
220
Sweden Sweden
1
Turkey Turkey
7
Ukraine Ukraine
121343576
United Kingdom United Kingdom
60705444
United States United States
722686412
Unknown Country Unknown Country
121343575
Vietnam Vietnam
164050

Downloads

China China
4229
France France
1
Germany Germany
-2134958943
Lithuania Lithuania
1
Russia Russia
4
Singapore Singapore
1081345991
Ukraine Ukraine
364026833
United Kingdom United Kingdom
1
United States United States
722686413
Unknown Country Unknown Country
203
Vietnam Vietnam
1

Files

File Size Format Downloads
Berezina.pdf 957.44 kB Adobe PDF 33104734

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.