Title Layered Structure of CoCrAlY/ZrSiO4/Al2O3 Coatings Before and After Thermal Treatment
Other Titles Структура покриття CoCrAlY/ZrSiO4/Al2O3 до та після термічної обробки
Authors Kovaleva, M.G.
Sirota, V.V.
Beresnev, V.M.
Tyurin, Yu.N.
Vagina, O.N.
Pavlenko, I.A.
ORCID
Keywords мікроструктура
мікротвердість
багатокамерний газодинамічний прискорювач
нікелеві сплави
термобар’єрні покриття
microstructure
microhardness
multi-chamber gas-dynamic accelerator
nickel alloys
thermal barrier coatings
Type Article
Date of Issue 2019
URI http://essuir.sumdu.edu.ua/handle/123456789/75425
Publisher Sumy State University
License
Citation Layered Structure of CoCrAlY/ZrSiO4/Al2O3 Coatings Before and After Thermal Treatment [Текст] = Структура покриття CoCrAlY/ZrSiO4/Al2O3 до та після термічної обробки / M.G. Kovaleva, V.V. Sirota, V.M. Beresnev [et al.] // Журнал нано- та електронної фізики. - 2019. - Т.11, № 6. - 06025. - DOI: 10.21272/jnep.11(6).06025.
Abstract У роботі щільні покриття CoCrAlY/ZrSiO4/Al2O3 були підготовлені на підкладках із суперсплавів на основі нікелю за допомогою нового багатокамерного газодинамічного прискорювача. Покриття піддавали термічній обробці у вакуумі при температурі 950 °С протягом 2 годин. Для аналізу хімічного складу використовували скануючий мікроскоп з мікрозондом EDX. Аналіз структурних змін, в основному з точки зору пористості, проводили за допомогою оптичного мікроскопа. Вимірювання мікротвердості покриття проводили за допомогою мікротвердоміра DM-8B з використанням пірамідки Вікерса при навантаженні 50 г. Встановлено, що термічна обробка позитивно впливає на мікроструктуру і мікротвердість покриття. Покриття CoCrAlY/ZrSiO4/Al2O3 після термічної обробки суцільні, без тріщин і добре пов’язані з підкладкою. Відсутність пор на межах розділу між різними шарами свідчить про хорошу адгезії між ними. Термічна обробка призвела до підвищення твердості покриття.
In work, dense CoCrAlY/ZrSiO4/Al2O3 coatings have been prepared on nickel based superalloy substrates by a new multi-chamber gas-dynamic accelerator. The coatings were subjected to thermal treatment in vacuum at a temperature of 950 °C for 2 hours. Scanning microscope with an EDX microprobe was used to analyze the chemical composition. Analysis of structural changes, mainly from the aspect of porosity, was also carried out using an optical microscope. Measurement of the microhardness of coatings was done with a microhardness tester DM-8B using a Vicker’s hardness tester at a test load of 50 g. A positive impact of thermal treatment on the coating microstructure and microhardness was observed. The CoCrAlY/ZrSiO4/Al2O3 coatings after thermal treatment were observed to be continuous, without cracks, and well bonded with the substrate. The absence of discontinuities in the interfaces among the different layers was indicative of good adhesion between them. Thermal treatment resulted in an increase in the coating hardness.
Appears in Collections: Журнал нано- та електронної фізики (Journal of nano- and electronic physics)

Views

China China
3768398
Germany Germany
17496
Greece Greece
1
Ireland Ireland
5261
Lithuania Lithuania
1
Mongolia Mongolia
1
Netherlands Netherlands
228
Sweden Sweden
1
Ukraine Ukraine
118473
United Kingdom United Kingdom
59465
United States United States
5474944
Unknown Country Unknown Country
118472
Vietnam Vietnam
915

Downloads

China China
1
Germany Germany
1
India India
1
Lithuania Lithuania
1
Ukraine Ukraine
355305
United Kingdom United Kingdom
1
United States United States
5474944
Unknown Country Unknown Country
3
Vietnam Vietnam
1

Files

File Size Format Downloads
Kovaleva_jnep_6_2019.pdf 374.25 kB Adobe PDF 5830258

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.