Title Effect of nickel on the structure and phase composition of the VCrMnFeCoNix high-entropy alloy
Authors Karpets’, M.V.
Myslyvchenko, Oleksandr Mykolaiovych
Makarenko, O.S.
Gorban, V.F.
Krapivka, M.O.
Dehula, Andrii Ivanovych  
Keywords сігма фаза
sigma phase
кристалічна структура
crystal structure
Type Article
Date of Issue 2015
Publisher Springer-Verlag
License In Copyright
Citation Effect of nickel on the structure and phase composition of the VCrMnFeCoNi x high-entropy alloy / M. V. Karpets’ et al. // Journal of Superhard Materials. 2015. Vol. 37, No. 3. P. 182–188. DOI: 10.3103/S1063457615030053
Abstract Вплив концентрації нікелю на фазовий склад, мікроструктуру і твердість досліджено високоентропійні сплави VCrMnFeCoNix (x = 0–3). Будова литої системи має складається з ГЦК твердого розчину та σ-фази, і обидві фази є багатокомпонентними. Це було знайдено що збільшення концентрації нікелю зменшує об’ємну частку σ-фази. Як результат зменшення кількості твердої σ-фази виявлено зменшення мікротвердості сплавів від 12 ГПа при x = 0 до 4,1 ГПа при x =3.
The effect of the nickel concentration on the phase composition, microstructure, and hardness of VCrMnFeCoNix (x = 0–3) high-entropy alloys has been studied. The structure of the cast system has been composed of fcc solid solution and σ-phase, and both phases are multicomponent. It has been found that an increase of the nickel concentration decreases the volume fraction of the σ-phase. As a result of the reduction of the amount of the solid σ-phase the microhardness of alloys has been detected to decrease from 12 GPa at x = 0 to 4.1 GPa at x =3.
Appears in Collections: Наукові видання (ТеСЕТ)


Japan Japan
Ukraine Ukraine
United States United States


United States United States


File Size Format Downloads
Karpets_sigma_phase.pdf 2,82 MB Adobe PDF 25

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.